黄端平
,
徐庆
,
陈文
,
王皓
,
袁润章
无机材料学报
采用甘氨酸-硝酸盐(GNP)法合成出La0.6Sr0.4Fe0.8Co0.2O3超细粉体,探讨各因素对产物的晶体结构和显微形貌的影响,研究烧成温度对电导率的影响.研究表明,G/Mn+控制在2.0—3.0、热处理温度为750℃是最佳的合成条件,1200℃烧成样品具有最优良的电性能.在室温～900℃温度范围内,样品的电导率在600℃附近出现最大值,低温段的导电行为符合小极化子导电机制.与常规固相法相比,GNP法制备样品具有更好的烧结活性和导电性能.
关键词:
La0.6Sr0.4Fe0.8Co0.2O3
,
perovskite-type oxides
,
glycine-nitrate process
,
electrical conductivity
李贵茂王恩刚张林左小伟赫冀成
金属学报
doi:10.3724/SP.J.1037.2010.00218
在有无磁场条件下进行了Cu-25%Ag(质量分数)合金的凝固实验, 研究了强磁场对Cu-25%Ag合金凝固组织中富Cu枝晶内部Ag析出相的影响, 测试了合金的硬度和电导率. 发现有无磁场条件下, 在不同大小的富Cu枝晶内部, Ag析出相的形态和尺寸各不相同, 大尺寸富Cu枝晶内部的Ag析出相呈连续的棒状结构, 小尺寸富Cu枝晶内部的Ag析出相呈非连续的颗粒状结构. 另外, 无磁场条件下析出的Ag相数量较多, 尺寸较细小; 有磁场条件下析出的Ag相数量较少, 尺寸较粗大. 受到Ag析出相的影响, 强磁场条件下合金的硬度降低, 电导率升高. 对强磁场下Ag析出相的影响机理进行了探讨, 并分析了析出相对合金硬度和电导率的影响机制.
关键词:
强磁场
,
Cu-25%Ag
,
Ag precipitate
,
hardness
,
electrical conductivity
郝红霞
,
刘瑞泉
无机材料学报
doi:10.3724/sp.j.1077.2009.00539
采用溶胶凝胶法合成了新型中温固体氧化物燃料电池(IT-SOFCs)阳极材料Ce1-xCoxOy（x＝0.10, 0.15, 0.20, 0.25, 0.30）(CDC)，并采用共压共烧结法制备了以NiO-CDC复合阳极为支撑、以Ce0.8Gd0.2O2-δ(GDC)为电解质、以La0.8Sr0.2Co0.8Fe0.2O3-δ(LSCF)- GDC为复合阴极的单电池. 利用XRD和SEM等方法对阳极材料进行了晶相结构、微观形貌和化学相容性等分析. 在400~700℃范围内，以加湿天然气（3％H2O）为燃料气，氧气为氧化气测试了电池的电化学性能. 结果表明：CDC阳极材料具有良好的孔道结构；八种不同阳极组成的单电池中50wt％NiO50wt%Ce0.8Co0.2Oy（C20C80）阳极支撑的单电池具有最佳的电化学性能，在650℃时其最大电流密度为148.84mA/cm2, 最大比功率为30.91mW/cm2.
关键词:
中温固体氧化物燃料电池
,
transition metal
,
cobaltdoped-ceria
,
electrical conductivity
魏亦军
,
陈永红
,
刘杏芹
,
孟广耀
无机材料学报
doi:10.3724/SP.J.1077.2006.01147
采用柠檬酸-硝酸盐法合成了Pr0.6-xNdxSr0.4FeO3-δ(x=0.0~0.6)系列钙钛矿型复合氧化物粉体, 用
XRD、FT-IR、TD-DTA、SEM等对产物的形成过程、物性及微结构进行了表征. 结果表明, 所合成的系列样品1200C煅烧2h即形成立方钙钛矿结构
的单相固溶体. 用直流四端子法测量了烧结陶瓷体在中温(450~800℃)范围内的电导率, A位单一稀土元素的样品(x=0.0、0.6)及以Pr(x=0.1)或
Nd(x=0.5)为主的稀土复合氧化物, 其电导率均在150S cm-1以上,明显高于双稀土样品(x=0.2、0.3、0.4)的数值( σ=45~80S cm-1); x=0.2、0.3
、0.4三个样品电导率较低的原因, 与它们在同样烧结制度下的致密度低密切相关.该系列样品的电导率在650~700℃附近出现最大值, 低温段的导电行为符合小极化子导电机制.
关键词:
双稀土
,
Pr0.6-xNdxSr0.4FeO3-δ
,
cathode materials
,
perovskite
,
electrical conductivity
曹悦
,
顾海涛
,
陈涵
,
郑益锋
,
周明
,
郭露村
无机材料学报
doi:10.3724/SP.J.1077.2010.00738
采用固相反应法合成了中温固体氧化物燃料电池阴极材料Pr2-xSrxCoO4+δ (x=0.8,1.0, 1.2). 通过XRD、SEM、热膨胀法、直流四探针法、交流阻抗谱法和循环伏安法对该体系材料的晶体结构、热膨胀系数、电导率和电化学性能进行了研究. 结果表明, 合成的粉体均形成了单相K2NiF4结构, Pr0.8Sr1.2CoO4+δ与电解质材料Sm0.2Ce0.8O1.9(SDC)在1100℃空气气氛下混合烧结, 未生成杂相. 材料的热膨胀系数随着Sr含量的增加而升高. 800℃时样品的电导率均大于100 S/cm. 随着Sr含量的增加, 极化电阻减小, Pr0.8Sr1.2CoO4+δ在空气中的极化电阻最小, 700℃为0.29 Ω·cm2.
关键词:
固体氧化物燃料电池
,
cathode
,
thermal expansion
,
electrical conductivity
,
electrochemical properties
Baoyun Liu Li Liu Nanlin Shi Jun Gong Chao Sun
材料科学技术（英）
The preparation of polyaniline nanofibers in aqueous solution was studied as functions of the concentrations and ratios of reactants. The morphology and microstructure of polyaniline nanofibers are affected by the concentrations and proportions of the reactants. A special kind of sea cucumber-like polyaniline nanofibers can be prepared under control of reaction conditions. Secondary growth is the formation mechanism. In addition, the bulk electrical conductivity of these sea cucumber-like polyaniline nanofibers was higher than that of other common polyaniline nanofibers.
关键词:
Polyaniline
,
nanofiber
,
aqueous solution method
,
morphology
,
electrical conductivity
Na Yin Hongchao Wang Chunlei Wang
材料科学技术（英）
Lanthanum ferrites ceramics La0.9A0.1FeO3 (A=Mg, Ca, Sr, Ba) have been prepared by solid state reaction. X-ray power diffraction analysis reveals that all samples are of pure perovskite structure with orthorhombic phase. Electrical conductivity and Seebeck coefficient have been measured in vacuum within the temperature range between room temperature and 800°C. The electrical conductivity shows semiconducting behavior. Temperature dependence of electrical conductivity indicates that adiabatic small-polaron hopping mechanism is dominant for their electric transportations. Seebeck coefficients are positive for samples, suggesting p-type conduction in the whole temperature range. The highest Seebeck coefficient is found to be 654 μV/K for La0.9Mg0.1 FeO3. Except La0.9Ba0.1FeO3, the electrical conductivity of La0.9A 0.1FeO3 increases with increasing atomic number of the A-site element, while Seebeck coefficient decreases.
关键词:
La0:9A0:1FeO3 ceramics
,
electrical conductivity
,
Seebeck coefficient
赵军
,
李冀蒙
,
赵陆民
,
尹硕
,
陈久川
,
文全兴
稀有金属
doi:10.13373/j.cnki.cjrm.2015.02.001
采用热常数测试仪和电导仪测试了 Cu-37.67Zn-1.43Al合金经1～5 GPa,700℃保温20 min处理前后的热导率和电导率,用光学显微镜和透射电镜对其组织特征进行观察,并探讨了高压热处理对Cu-37.67Zn-1.43Al合金导热性能和导电性能的影响.结果表明:退火态Cu-37.67Zn-1.43Al合金的原始组织由α相和少量的β相组成.经高压热处理后,合金组织中白色块状α相数量减少,出现细条状α相,组织明显细化,细化效果随压力的增大先增强后减弱,当压力为3 GPa时,组织细化效果最好.并且,高压热处理能降低Cu-37.67Zn-1.43Al合金的热导率和电导率,在1～5 GPa范围内,随着压力的增大,该合金的热导率和电导率均先降低后升高;压力为3 GPa时,热导率和电导率均达到最低值,分别为99 W·m-1·K-1和20.86％ IACS,较高压处理前分别降低了14.66％和15.07％,但经高压处理与未经高压处理的样品热导率差值随着温度的升高而逐渐减小,在25℃时,两者的差值为17 W·m-1·K-1,而在400℃时,两者的差值为4 W·m-1·K-1.其原因主要是高压热处理后Cu-37.67Zn-1.43Al合金组织细化及组织内位错密度增大.
关键词:
Cu-37.67Zn-1.43Al合金
,
高压热处理
,
热导率
,
电导率
邹军涛
,
李阳
,
雷春娟
,
杨鑫
,
杨晓红
,
王献辉
材料热处理学报
通过在铜基体中添加V0.97W0.03O2制备了具有相变效应的Cu/V0.97W0.03O2复合材料,研究了添加相V0.97W0.03O2相变以及在Cu基体中的弥散程度对Cu/V0.97W0.03O2复合材料电导率的影响.采用场发射扫描电镜表征复合材料组织特征,利用X-ray衍射分析复合材料物相组成,并利用电导率测量系统检测不同温度下Cu/V0.97W0.03O2复合材料的电导率.结果表明,随高能球磨时间增加,铜基体中V0.97W0.03O2颗粒粒径越小,分布越弥散,对Cu/V0.97W0.03O2复合材料的电导率影响越明显.铜基体中的添加相V0.97W0.03O2会在0℃附近发生相变,导致Cu/V0.97W0.03O2复合材料相变前后的电导率变化幅度由5.41％升高到26.88％,相变效应增加明显.
关键词:
二氧化钒
,
高能球磨
,
相变
,
电导率